Both the shape and size of metal nanoparticles are key factors in determining the coupling efficiency. The two-layer ultrathin nanofilm increases the nanoparticle density; according to the Mie theory, the extinction coefficient is proportional to the nanoparticle density. Consequently, optical local-field SGC-CBP30 in vivo enhancement of
the two-layer continuous ultrathin gold nanofilm is stronger than that of the one-layer ultrathin continuous gold nanofilm. Figure 3 embodies selleck compound the absorbance of the two-layer ultrathin continuous gold nanofilm which far outweighs that of ITO/PEDOT:PSS/Au film/P3HT:PCBM and ITO/Au film/PEDOT:PSS/P3HT:PCBM. In brief, the enhanced efficiency is shown to stem from field enhancement originating both from localized plasmonic resonances and periodic similar nanopatch antenna configuration and SPP modes in the peculiar gold nanofilm. To investigate the performance for electromagnetic enhancement, SERS spectroscopic measurements
were carried out using Rhodamine 6G, a well-characterized test molecule. Spectra obtained from Rhodamine 6G molecules at a concentration of 10−3 to 10−6 M are shown in Figure 4 which exhibit repeatable high SERS sensitivity. The distances between the centers of two adjacent particles and the particle diameter are important parameters affecting SERS activity. This ultrathin continuous gold nanofilm MDV3100 ic50 produces a high Raman signal due to its periodic arrangements, high nanoisland density, and control of the gap between the nanostructures in the sub-10-nm regime. The observed SERS efficiency
can be explained in terms of interparticle coupling-induced Raman enhancement. Thus, the distinctive continuous gold nanofilm is very effective in providing abundant hot spots for SERS enhancement. Dolutegravir Conclusions In conclusion, we have produced continuous ultrathin gold nanofilms with high local-field enhancement effect and a high SERS activity. Spectral analysis suggests that the prominent light absorption in organic photosensitive materials and the high SERS activity arise from the near-field effect of localized surface plasmons of nanoparticles. Owing to their distinctive morphology and high light transmittance, continuous ultrathin gold nanofilms can be used in multilayer organic solar cells to trap light without affecting the physical thickness of solar photovoltaic absorber layers and yielding new options for solar cell design. Further work is needed to research two-dimensional distinctive continuous gold nanofilms that are utilized to trap light in solar cells which may be suitable for application to the high photoelectric conversion efficiency of organic solar cells. Acknowledgements This work is supported by NSFC under grant no.